PA66 RFP36XXZ沙伯基礎創新內部潤滑含玻璃纖維有機硅PTFE尼龍66塑料（18024445500）




Also known as:LNP™LUBRICOMP™Compound RFL-4536 LEXBK8-115


Product reorder name:RFP36XXZ


　


LNP LUBRICOMP RFP36XXZ is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: internally lubricated. Also known as LUBRICOMP RFL-4536 LEX


　







Property

　




TYPICAL PROPERTIES (1)


MECHANICAL

Value

Unit

Standard




Tensile Stress, brk, Type I, 5 mm/min

1350

kgf/cm²

ASTM D 638




Tensile Strain, brk, Type I, 5 mm/min

2.1

%

ASTM D 638




Tensile Modulus, 50 mm/min

106800

kgf/cm²

ASTM D 638




Flexural Stress, yld, 1.3 mm/min, 50 mm span

1980

kgf/cm²

ASTM D 790




Flexural Modulus, 1.3 mm/min, 50 mm span

77200

kgf/cm²

ASTM D 790




Tensile Stress, break, 5 mm/min

135

MPa

ISO 527




Tensile Strain, break, 5 mm/min

2.2

%

ISO 527




Tensile Modulus, 1 mm/min

9400

MPa

ISO 527




Flexural Stress, yield, 2 mm/min

207

MPa

ISO 178




Flexural Modulus, 2 mm/min

9400

MPa

ISO 178




IMPACT

Value

Unit

Standard




Izod Impact, unnotched, 23°C

79

cm-kgf/cm

ASTM D 4812




Izod Impact, notched, 23°C

14

cm-kgf/cm

ASTM D 256




Instrumented Impact Energy @ peak, 23°C

71

cm-kgf

ASTM D 3763




Izod Impact, unnotched 80*10*4 +23°C

50

kJ/m²

ISO 180/1U




Izod Impact, notched 80*10*4 +23°C

9

kJ/m²

ISO 180/1A




THERMAL

Value

Unit

Standard




HDT, 1.82 MPa, 3.2mm, unannealed

233

°C

ASTM D 648




HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

236

°C

ISO 75/Af




PHYSICAL

Value

Unit

Standard




Density

1.48

g/cm³

ASTM D 792




Moisture Absorption, 50% RH, 24 hrs

0.78

%

ASTM D 570




Mold Shrinkage, flow, 24 hrs (5)

0.2

%

ASTM D 955




Mold Shrinkage, xflow, 24 hrs (5)

1

%

ASTM D 955




Wear Factor Washer

11

10^-10 in^5-min/ft-lb-hr

ASTM D 3702 Modified




Dynamic COF

0.56

-

ASTM D 3702 Modified




Static COF

0.46

-

ASTM D 3702 Modified




Density

1.48

g/cm³

ISO 1183




Moisture Absorption (23°C / 50% RH)

1.22

%

ISO 62






Source GMD, last updated:2008/10/30




Processing




Parameter


Injection Molding

Value

Unit


Drying Temperature

80

°C


Drying Time

4

hrs


Maximum Moisture Content

0.15 - 0.25

%


Melt Temperature

280 - 305

°C


Front - Zone 3 Temperature

295 - 305

°C


Middle - Zone 2 Temperature

280 - 295

°C


Rear - Zone 1 Temperature

265 - 275

°C


Mold Temperature

95 - 110

°C


Back Pressure

0.2 - 0.3

MPa


Screw Speed

30 - 60

rpm




Source GMD, last updated:2008/10/30




　


THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.





供應的沙伯基礎PA66塑料如下：


LNP™ LUBRICOMP Compound




Grades

Description


RA004

Internally Lubricated Nylon 66 compound containing Aramid.



RAL22

Internally Lubricated Nylon 66 compound containing Aramid, PTFE.



RAL22I

Internally Lubricated, High Impact Nylon 66 compound containing PTFE, Aramid Fiber.



RAL22S

Internally Lubricated Nylon 66 compound containing PTFE, Aramid Fiber.



RAL23

Internally Lubricated Nylon 66 compound containing Aramid Fiber, PTFE.



RAL23S

Heat Stabilized Nylon 66 compound containing Aramid Fiber, PTFE.



RCL36S

Electrically Conductive Nylon 66 compound containing Carbon Fiber, PTFE.
:


RCP36

Electrically Conductive Nylon 66 compound containing Silicone, PTFE, Carbon Fiber.



RFL16

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.



RFL26S

Internally Lubricated, Heat Stabilized Nylon 66 compound containing Glass Fiber, PTFE.



RFL33

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.


RFL34

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.


RFL36L

Internally Lubricated, Low Extractible Nylon 66 compound containing Glass Fiber, PTFE.


RFP36

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.


RFP36XXZ

PA 66, Silicone, Lubricants, PTFE, Glass, Internally Lubricated, Wear resistant,


RN001S

Internally Lubricated, Heat Stabilized Nylon 66 compound containing MOS2.


RP003

Internally Lubricated Nylon 66 compound containing PTFE, Silicone.


RP004

Internally Lubricated Nylon 66 compound containing PTFE, Silicone.


RX01514

Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).


RX03643H

Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).


RX05496

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.


RX06480

Internally Lubricated Nylon 66 compound containing PTFE, Glass Fiber, Silicone.


RX85514

Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).