PA6 BC 550 Z DUSXBL 900116德國朗盛Durethan吹塑耐熱老化穩定尼龍6塑料（18024445500）

PA 6, non-reinforced, blow molding, improved impact strength, heat-aging stabilized



ISO Shortname: ISO 1874-PA 6-HI, BHR, 14-020

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 1.5　
C Molding shrinkage, transverse 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 1.5　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 2000 430
C Yield stress 50 mm/min MPa ISO 527-1,-2 50　
C Yield strain 50 mm/min % ISO 527-1,-2 4.0　
C Nominal strain at break 50 mm/min % ISO 527-1,-2 140 165
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N N
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 100 130
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 25 25
Izod impact strength 23 °C kJ/m² ISO 180-1U N N
Izod impact strength -30 °C kJ/m² ISO 180-1U N N
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 85 105
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 25 25
Flexural modulus 2 mm/min MPa ISO 178-A 1800 470